    Influence of time and hydration (ageing) on flexural strength of Yttrium stabilized Zirconia polycrystals (Y-TZP) fabricated with different CAD-CAM Systems.

    • Khulud A Al-Aali, Saad Alresayes, Aasem M Alhenaki, Fahim Vohra, and Tariq Abduljabbar.
    • Khulud A. Al Aali, Department of Clinical Dental Sciences, College of Dentistry, Princess Nourah Bint Abdulrahman University, Riyadh, Saudi Arabia.
    • Pak J Med Sci. 2021 May 1; 37 (3): 833-839.

    ObjectivesTo evaluate the effect of time and hydration (ageing) on flexural strength of yttrium-stabilized zirconia polycrystals (Y-TZP) zirconia fabricated from three different materials.MethodsThis in-vitro study was performed from June to September 2019. Y-TZP bars, measuring 2 x 3 x 20 mm were prepared and sintered from three different materials, Group-1: LAVA™ Zirconia (3M ESPE, US) (control) Group-2: Vita In-Ceram YZ (VITA, Germany) and Group-3: Aadva™ Zirconia (Zr) (GC Advanced technologies Inc.). 30 zirconia bars per group were prepared using sectioning of blocks with isomet saw. Followed by sintering in furnaces for recommended temperature cycles. One side of bars were polished and beveled for flexural testing. Groups of specimens were divided into subgroups of 3 (n=10) based on the ageing (distilled water in the incubator at 37ºC) durations (48 Hrs and two and half years). Ten specimens in each material groups were not aged (controls). Samples were exposed to a static force in a three-point bend test using a universal instron-testing machine until fracture. Scanning electron microscopic assessment was performed for fractured specimens for ageing. Data was analyzed using ANOVA and Tukey post hoc test.ResultsThe mean flexural strength at baseline for Group-1: LAVA™ Zirconia, group (632.7 ± 136.5 MPa) 2: Vita In-Ceram YZ (1036.3 ± 229.6 MPa), and Group-3: Aadva™ Zirconia (1171.3 ± 266.3 MPa) were significantly different. Group-2 and Group-3 specimens showed higher strength compared to Group-1 specimens, irrespective of the ageing duration (p<0.05). Analysis of pooled data for flexural strength for materials by aging period (baseline, after 48 hours and after 2 and ½ years) showed that there was significant reduction of strength with increasing duration (p<0.05).ConclusionsY-TZP showed variations in flexural strength depending on the material type. Ageing duration exhibited significant influence on the flexural strength of Y-TZP when comparing no ageing to two and half years. Vita In-Ceram YZ and Aadva Zirconia (Zr) showed higher and clinically acceptable flexural strength outcomes.Copyright: © Pakistan Journal of Medical Sciences.

      Pubmed     Copy Citation     Plaintext  

      Add institutional full text...

    Notes

     
    Knowledge, pearl, summary or comment to share?
    300 characters remaining
    help        
    You can also include formatting, links, images and footnotes in your notes
    • Simple formatting can be added to notes, such as *italics*, _underline_ or **bold**.
    • Superscript can be denoted by <sup>text</sup> and subscript <sub>text</sub>.
    • Numbered or bulleted lists can be created using either numbered lines 1. 2. 3., hyphens - or asterisks *.
    • Links can be included with: [my link to pubmed](http://pubmed.com)
    • Images can be included with: ![alt text](https://bestmedicaljournal.com/study_graph.jpg "Image Title Text")
    • For footnotes use [^1](This is a footnote.) inline.
    • Or use an inline reference [^1] to refer to a longer footnote elseweher in the document [^1]: This is a long footnote..

    hide…